>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Ned Simmons on July 7, 2006, 7:30 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Gunner on July 7, 2006, 11:50 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Karl Townsend on July 8, 2006, 7:10 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Eric R Snow on July 8, 2006, 1:35 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | >>>>>>>>>>>>>>Make $5000 Online Without Investment | November 23, 2007, 11:01 pm |
| Re: Grizzly G8689 vs. Sherline 5000 : opinions ? | June 3, 2007, 6:42 pm |
| Re: Grizzly G8689 vs. Sherline 5000 : opinions ? | June 4, 2007, 6:20 am |
| Earn $5000 per month with the Excellent Money Making Programs | November 28, 2007, 10:56 am |
| Rockwell Allen Bradley Programming Software, RSLogix 5, RSLogix 500, RS Linx, RSLogix 5000, version 2007, 1 DVD | July 23, 2007, 12:40 pm |
| Webcool24.com : Biggest worldwide Asian free Video multi language web , Travel, Sports, Massages techniques, Fashions, Jokes , Top models , Free online IT learning , 5000 links, 250 free online TV , 50000 music video, nice landscapes , Health , Fl | August 14, 2007, 10:17 am |
| Re: bearing help. | October 23, 2007, 9:19 am |
| Re: bearing help. | October 25, 2007, 1:22 am |
| Ball bearing fit... | July 27, 2006, 10:28 am |
| Tube, bearing rod | November 13, 2006, 9:10 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore