A question for the group MikeMandaville 08-23-2007
Posted by MikeMandaville on August 23, 2007, 8:03 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Stephen Robinson on August 23, 2007, 8:46 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Lloyd E. Sponenburgh on August 23, 2007, 8:53 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Paul K. Dickman on August 23, 2007, 11:28 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Lloyd E. Sponenburgh on August 23, 2007, 11:45 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Group question September 14, 2008, 1:18 am
metal question for the group January 18, 2008, 9:48 am
Re: metal question for the group January 18, 2008, 1:34 pm
another question, since this group solved my last problem (radiusing without a rotary table) April 6, 2008, 2:44 pm
New to group June 10, 2007, 3:37 pm
Need Help from the Group July 3, 2007, 1:09 pm
New to group September 15, 2007, 11:21 pm
joing my group March 9, 2007, 5:44 am
join me in this group June 1, 2007, 9:53 am
is it me? (group size?) March 4, 2008, 6:41 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap