Anodizing and Powdercoat Compatibility Questions Weyland 10-01-2006
Posted by Weyland on October 1, 2006, 9:23 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Harold and Susan Vordos on October 2, 2006, 3:47 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Weyland on October 2, 2006, 10:23 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Harold and Susan Vordos on October 3, 2006, 12:56 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
how to keep powdercoat from peeling? April 24, 2008, 12:16 am
very black anodizing November 4, 2006, 12:10 am
Anodizing question December 6, 2006, 5:32 pm
anodizing kits? January 5, 2008, 5:46 pm
Large Capacity Anodizing November 3, 2006, 9:37 pm
Removing Aluminum From Anodizing? May 4, 2008, 8:43 pm
Surface roughness after hard anodizing April 19, 2006, 11:26 am
Re: A little plating and anodizing current regulator March 14, 2006, 12:41 am
Re: A little plating and anodizing current regulator March 14, 2006, 2:20 am
Re: Getting An Enclosed Trailer...Questions, Questions, Questions December 21, 2007, 12:06 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap