Posted by Ignoramus23763 on February 18, 2007, 3:21 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Wayne on February 18, 2007, 3:30 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by on February 18, 2007, 5:42 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ignoramus23763 on February 18, 2007, 6:35 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by on February 18, 2007, 6:49 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Metal brake question June 29, 2008, 11:51 am
3 in 1 roll/brake/shear question March 24, 2008, 1:38 pm
question on bending .040 aluminum on a brake July 24, 2008, 10:09 am
dc motor controller March 17, 2006, 5:10 pm
FA: GE 550T + u-Stor parting out HNC controller May 5, 2007, 11:16 am
Shaded pole foot controller? November 26, 2007, 10:49 pm
Treadmill motor/controller Potentiometer? April 27, 2006, 9:09 pm
DC Motor Controller "Inhibit Circuit"? December 30, 2007, 10:29 pm
little hope, need to fix or replace a model MC-45 motor controller August 17, 2006, 10:15 pm
oven/kiln controller that can be hooked to your computer December 31, 2006, 12:46 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap