Posted by RoyJ on November 17, 2006, 11:38 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Scott S. Logan on November 18, 2006, 11:08 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by RoyJ on November 18, 2006, 3:45 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Errol Groff on November 18, 2006, 7:52 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Martin H. Eastburn on November 18, 2006, 8:43 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | thanks Scott Logan | September 26, 2007, 8:26 pm |
| Calling all you chemists... | May 14, 2008, 11:47 am |
| are you isolated, I mean, calling between instant productions | August 12, 2007, 7:31 pm |
| 10" Logan $230!!!! | December 5, 2006, 5:17 pm |
| Logan lathe | November 3, 2007, 12:16 am |
| Logan 7" Shaper | May 8, 2006, 9:29 pm |
| Need 3 jaw chuck for logan 10" | January 22, 2008, 12:04 am |
| thoughts on Logan lathes? | August 16, 2006, 2:11 am |
| FS: LOGAN 10" BENCH LATHE | September 19, 2006, 10:14 am |
| Logan Lathe Gloat | October 21, 2006, 12:56 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore