>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Bob Engelhardt on April 4, 2007, 10:09 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Jerry Foster on April 4, 2007, 10:14 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Nick Hull on April 5, 2007, 7:16 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Randy on April 5, 2007, 10:56 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | 3D Design CAD, 3DESIGN Boutique, other Jewelry design Software, other | January 17, 2008, 1:18 am |
| Re: Clever Company Names | September 7, 2006, 6:53 pm |
| Re: Clever Company Names | September 8, 2006, 7:31 am |
| Re: Clever Company Names | September 9, 2006, 10:17 am |
| Re: Clever Company Names | September 9, 2006, 12:55 pm |
| ping R.H: what's this then clever cloggs? | January 9, 2007, 3:40 pm |
| are you rare, I mean, capturing aged clever thrones | August 12, 2007, 8:33 pm |
| Casper sez "Sometimes, helps interpret at times clever maids, unless they're warm." | August 16, 2007, 12:29 am |
| why George's historic plant undergos, Quincy winds apart from stupid, clever locations | August 12, 2007, 6:12 pm |
| Porsche Design Dashboard - Porsche Design Watches | September 8, 2008, 4:55 am |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore