Cold saw vs. bandsaw Louis Ohland 04-24-2007
Posted by Louis Ohland on April 24, 2007, 1:40 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Grant Erwin on April 24, 2007, 1:54 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Louis Ohland on April 24, 2007, 2:04 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Grant Erwin on April 24, 2007, 4:33 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Louis Ohland on April 24, 2007, 10:19 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Bandsaw vs cold saw November 27, 2008, 11:09 am
Hot or cold cutting? Hack a cutoff saw to cold saw? August 8, 2007, 3:20 pm
Horizontal bandsaw vs vertical bandsaw April 28, 2007, 8:46 pm
FS - Bandsaw September 22, 2007, 4:20 pm
bandsaw help March 14, 2008, 12:26 am
Bandsaw MOtor Help July 23, 2006, 4:00 pm
Junk HF bandsaw November 27, 2006, 11:49 pm
Bandsaw pictures March 18, 2007, 5:43 pm
bandsaw 304 stainless April 4, 2007, 9:26 am
Bandsaw blade Q, and tip. April 21, 2007, 10:53 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap