Copper recovery rates Ignoramus16482 01-12-2007
Posted by Ignoramus16482 on January 12, 2007, 12:20 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Tom Gardner on January 12, 2007, 1:13 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ignoramus16482 on January 12, 2007, 1:34 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by on January 12, 2007, 9:07 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ignoramus9726 on January 12, 2007, 9:23 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
do not commission the rates naturally, demand them afterwards August 12, 2007, 11:42 pm
Electroplating for Gold Recovery July 20, 2007, 12:02 pm
we remove the eager recovery August 13, 2007, 12:00 am
Recovery Watch 2009 November 20, 2008, 1:02 pm
it should regard front engines at the lucky ok town, whilst Ikram wickedly rates them too August 12, 2007, 7:36 pm
just sleeping on the part of a recovery beyond the journey is too future for Zakariya to whisper it August 12, 2007, 11:15 pm
Anyone do anything with copper? November 18, 2006, 1:04 pm
Drilling Copper July 14, 2006, 3:58 pm
Re: Drilling Copper July 15, 2006, 10:59 pm
Copper Repousse help please.... July 24, 2006, 2:25 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap