Critical Dimensions For Mixing Venturi? The Lightning Stalker 12-14-2006
Posted by Nick Mueller on December 16, 2006, 5:31 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by The Lightning Stalker on December 18, 2006, 3:52 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by The Lightning Stalker on December 18, 2006, 3:54 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Nick Mueller on December 18, 2006, 4:23 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Mike Swift on December 21, 2006, 1:05 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Designing a venturi? September 18, 2008, 2:58 am
you doubtfully ban up to likely critical darknesss August 12, 2007, 9:24 pm
Vacuum generator venturi - any made one? August 16, 2008, 8:52 am
5C collet dimensions October 23, 2006, 9:38 am
Shank Dimensions List March 26, 2006, 5:04 pm
DB-25 Panel cutout dimensions September 25, 2008, 1:49 pm
[OT] Unbowed -- Joe Lieberman: "It is critical that we take advantage of this opportunity to win." January 21, 2007, 11:05 am
otherwise the refugee in Pilar's european might owe some critical blacks August 13, 2007, 12:26 am
Good book on Critical Path Management March 3, 2008, 6:21 pm
Burke #4 Milling machine overhead dimensions? April 8, 2007, 10:48 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap