Cross Posted - Somewhat on topic for all... Joe AutoDrill 01-30-2007
Posted by Larry Jaques on January 31, 2007, 8:35 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Joe AutoDrill on January 31, 2007, 8:07 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ron Thompson on January 31, 2007, 9:31 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Joe AutoDrill on January 31, 2007, 9:42 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ron Thompson on January 31, 2007, 9:51 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Cross-Posted HD-DVD Key thread May 6, 2007, 11:44 am
Not sure if I ever posted this here... May 22, 2007, 3:35 pm
using the drop box - files never posted March 9, 2008, 11:59 am
I posted some pictures of the newest addition to my shop March 27, 2006, 11:33 pm
Clausing 5914 Manual posted to the dropbox July 3, 2008, 5:36 pm
UH-oh! drill press countershaft 'geometery problem' is developing - pix posted July 15, 2006, 2:42 pm
worm gear WINCH "worm slop" problem (is something missing?) - MPEG *movie* posted to illustrate... July 7, 2007, 1:55 pm
OT Cross posting September 15, 2006, 6:02 pm
cross stitching May 22, 2008, 4:12 pm
using a DC motor as a generator, for an AC motor-driven DC welder (pix posted) May 21, 2008, 4:34 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap