Cutting hardened Gears oldjag 04-29-2007
Posted by john on April 30, 2007, 10:37 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by oldjag on May 2, 2007, 12:26 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Steve Austin on May 2, 2007, 8:59 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by John on May 2, 2007, 8:34 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ned Simmons on April 30, 2007, 11:44 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
cutting a keyway in a hardened & ground shaft July 24, 2006, 10:20 pm
Cutting Involute Gears May 2, 2008, 3:07 pm
cutting small involute spur gears January 26, 2007, 4:23 pm
Hardened lock shackles? April 29, 2007, 12:04 am
Turning 4140 Pre Hardened June 23, 2007, 10:46 am
Soaped, hardened parts have less scale. Why? November 5, 2006, 12:28 am
"Unhardening" hardened punches to deform them May 14, 2007, 8:42 am
hardened gear on a mild shaft September 28, 2008, 12:52 am
Re: Drilling hardened carbon steel set screw? July 12, 2006, 4:17 pm
Help! Drilling out a broken 6-32 hardened steel set screw... December 3, 2006, 1:21 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap