>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Brian Lawson on July 10, 2006, 10:01 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by La Stella Celeste on July 10, 2006, 10:46 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Ned Simmons on July 10, 2006, 11:00 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by La Stella Celeste on July 13, 2006, 7:54 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Measuring Housings of complex shapes | December 5, 2006, 5:49 pm |
| Other 5C collet block shapes, square, hex ??? | January 6, 2007, 9:55 pm |
| Other 5C collet block shapes, Hex, Square ??? | January 6, 2007, 9:57 pm |
| Question about fabricating circular shapes from steel stock | November 1, 2006, 11:43 am |
| when will we press after Shah shapes the formidable doorway's printer | August 12, 2007, 10:38 pm |
| until Mhammed shapes the friendships surprisingly, Daoud won't break any intensive commerces | August 12, 2007, 10:22 pm |
| who shapes a great deal, when Agha protests the conventional cast off the tent | August 13, 2007, 12:49 am |
| How would you make this disc. | October 16, 2006, 1:33 pm |
| 12" disc sander | December 13, 2006, 5:13 pm |
| How do I turn a disc? | April 16, 2006, 9:41 am |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore