Posted by Tom Gardner on July 29, 2006, 6:49 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Ned Simmons on July 29, 2006, 7:39 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Anthony on July 29, 2006, 11:33 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Steve R. on July 30, 2006, 4:13 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by John on July 30, 2006, 4:57 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | shank adapter, extension rod, button bit, thread bit,taper bit, taper rod, drill rod, drill bit, corss bit, chisel bit, DTH hammer drilling ,rock drill, drill tube, casing shoe, drilling tool, core bit, core barrel, ODEX, TUBEX, quarrying,mining equipment | September 8, 2006, 2:22 am |
| Bad Drill Bits!!! If you don't have a Darex Drill Doctor, read at your own risk of failing to understand. | December 12, 2007, 4:16 pm |
| How can I automatically tap 500 holes in 5/16-18 thread size using a hand drill or drill press? | January 1, 2008, 6:18 pm |
| Drill Rob for Drill Press Runout | July 4, 2006, 1:04 pm |
| MT2 drill bits vs. MT2 drill press | August 30, 2006, 2:33 am |
| please ID this drill bit | January 15, 2007, 11:32 pm |
| Drill Jig Name | January 24, 2008, 3:20 pm |
| Re: Which HF drill press? Or neither? | September 8, 2006, 9:01 pm |
| Re: Which HF drill press? Or neither? | September 10, 2006, 3:05 am |
| More on drill bits over 5/8" | September 17, 2006, 7:36 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore