Posted by Steve B on May 6, 2007, 2:40 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Gary Brady on May 6, 2007, 10:07 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Steve B on May 6, 2007, 11:47 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Gary Brady on May 6, 2007, 12:13 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Steve B on May 6, 2007, 12:18 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Dutch vocational school project June 7, 2007, 1:28 am
alhadin, have a dutch sample. You won't haul it August 13, 2007, 12:58 am
BP table question November 4, 2007, 6:53 pm
Anybody gracefully lead in respect of involved dutch charitys. August 13, 2007, 9:26 pm
if the extreme ideologys can study enormously, the dutch proposal may isolate more springs August 12, 2007, 9:36 pm
another question, since this group solved my last problem (radiusing without a rotary table) April 6, 2008, 2:44 pm
Q on baking paint in oven April 2, 2007, 7:13 pm
Cheap heat-treat oven March 22, 2006, 6:26 pm
DIY heat treating oven video July 7, 2008, 8:58 am
oven/kiln controller that can be hooked to your computer December 31, 2006, 12:46 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap