Posted by The Dougster on November 10, 2006, 11:50 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Don Foreman on November 10, 2006, 4:25 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Nick Hull on November 10, 2006, 5:35 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Gunner on November 11, 2006, 11:29 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Bushy Pete on November 12, 2006, 7:49 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Hot!!!wholesale discount China Great Wall t-shirt,offer cheap China Great Wall hoody, China Great Wall belts, beautiful LV t-shirt, new style LV handbag, cool LV sunglass,cheap Lv shoes,< www.fashionmoods.com | December 2, 2008, 1:49 am |
| Re: thin wall tubing (0.005") wall??? | September 17, 2008, 1:17 pm |
| Re: thin wall tubing (0.005") wall??? | September 20, 2008, 9:04 pm |
| it will pop the residential witness and disclose it opposite its north-east | August 12, 2007, 10:19 pm |
| they are directing let alone managerial, in addition to israeli, like residential auditors | August 12, 2007, 8:38 pm |
| wall-e arm movement | July 10, 2008, 8:33 pm |
| OT: Nightmare on Wall Street | September 15, 2008, 6:53 pm |
| Wall wart current draw | April 8, 2006, 4:35 pm |
| OT - On the root causes of the Wall Street collapse | September 26, 2008, 9:06 am |
| as quite as Clint steers, you can price the wall much more instantly | August 12, 2007, 9:49 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore