HF Blade Welder Proctologically Violated©® 10-26-2006
Posted by Proctologically Violated©® on October 26, 2006, 7:14 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by werty on October 29, 2006, 4:39 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Proctologically Violated©® on October 29, 2006, 5:36 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Gunner on October 29, 2006, 9:55 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by rashid111 on October 30, 2006, 11:46 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
inexpensive bandsaw blade welder? April 12, 2007, 5:15 pm
Solder or heat shrink and brazing with a MIG welder, Century Solar 2150 welder January 8, 2007, 1:38 am
Turning a AC welder into a DC welder questions. March 8, 2007, 9:20 am
band saw blade August 3, 2006, 9:32 pm
Band saw blade October 26, 2006, 1:07 pm
Bandsaw blade Q, and tip. April 21, 2007, 10:53 am
what's happening between blade and steel? October 26, 2006, 11:50 am
WTB Broken band saw blade January 15, 2007, 9:00 am
How to fold a bandsaw blade May 16, 2007, 3:36 pm
Can I save my bandsaw blade? December 27, 2007, 5:21 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap