Holding a disc to jaws / faceplate greg 08-16-2006
Posted by on August 16, 2006, 2:07 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Rob on August 16, 2006, 6:43 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by gdenehy on August 16, 2006, 8:36 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Rob on August 16, 2006, 9:09 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Jordan on August 16, 2006, 10:30 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Why curved slots in faceplate? April 17, 2007, 8:26 pm
Setting up faceplate for boring job... December 5, 2007, 7:44 am
How would you make this disc. October 16, 2006, 1:33 pm
12" disc sander December 13, 2006, 5:13 pm
How do I turn a disc? April 16, 2006, 9:41 am
Re: Holding a cone in the lathe.... March 11, 2008, 1:59 am
Disc cutter - other shapes? July 10, 2006, 8:48 am
Need 4" Carbide disc or ring June 25, 2007, 8:41 pm
Re: 12" Disc Sander reccomendations October 28, 2007, 3:29 pm
Re: 12" Disc Sander reccomendations October 28, 2007, 5:11 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap