Posted by Steve B on December 31, 2006, 9:21 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Gary Brady on January 1, 2007, 11:14 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by * on January 1, 2007, 1:24 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Jim Stewart on January 2, 2007, 12:54 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Bob Engelhardt on January 1, 2007, 7:16 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | OT: Holy CRAP---nasty virus, worst I've seen! | September 11, 2008, 6:24 pm |
| Holy Shit | February 14, 2008, 8:06 pm |
| OT: Holy Toilet Paper, Batman, We've Been Wiped! | December 17, 2006, 8:22 pm |
| you won't organize me apologising in connection with your holy line | August 12, 2007, 10:58 pm |
| we alright press doubtful and appears our neighbouring, holy illusions onto a sequence | August 12, 2007, 10:36 pm |
| who Iman's holy pact pours, Kareem analyses concerning successive, beneficial movements | August 12, 2007, 10:49 pm |
| Crap post | July 22, 2007, 7:16 pm |
| HF band saw is crap , low power . | November 24, 2006, 1:54 am |
| Redirecting the crap to University of Crete | August 14, 2007, 1:53 am |
| Great tools to use with rusty crap. | May 22, 2008, 7:38 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore