>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Snag on November 24, 2006, 8:12 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Andrew VK3BFA on November 24, 2006, 8:19 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Nick Mueller on November 24, 2006, 9:07 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Norman Billingham on November 24, 2006, 8:41 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Help indentifing a machine taper | May 10, 2008, 1:34 am |
| Making taper attachment for lathe - what range of taper? | August 28, 2006, 8:33 am |
| shank adapter, extension rod, button bit, thread bit,taper bit, taper rod, drill rod, drill bit, corss bit, chisel bit, DTH hammer drilling ,rock drill, drill tube, casing shoe, drilling tool, core bit, core barrel, ODEX, TUBEX, quarrying,mining equipment | September 8, 2006, 2:22 am |
| JD tie rod end taper? | June 14, 2008, 8:44 pm |
| TAPER ATTACHMENT | February 10, 2007, 4:50 am |
| NST40 Taper? | February 27, 2007, 1:31 pm |
| Taper tolerances | August 6, 2007, 3:03 pm |
| Re: Taper tolerances | August 7, 2007, 2:38 pm |
| Re: Boring a taper | March 12, 2006, 8:33 am |
| Re: Boring a taper | March 13, 2006, 2:21 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore