How would you make this disc. Roger Haar 10-16-2006
Posted by Roger Haar on October 16, 2006, 1:33 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Tim Wescott on October 16, 2006, 2:08 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by on October 16, 2006, 2:25 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by steamer on October 17, 2006, 11:45 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by on October 16, 2006, 2:28 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
12" disc sander December 13, 2006, 5:13 pm
How do I turn a disc? April 16, 2006, 9:41 am
Disc cutter - other shapes? July 10, 2006, 8:48 am
Need 4" Carbide disc or ring June 25, 2007, 8:41 pm
Re: 12" Disc Sander reccomendations October 28, 2007, 3:29 pm
Re: 12" Disc Sander reccomendations October 28, 2007, 5:11 pm
Re: 12" Disc Sander reccomendations October 28, 2007, 10:10 pm
Drag from disc brake? November 11, 2007, 8:12 pm
Holding a disc to jaws / faceplate August 16, 2006, 2:07 am
source for replacement friction disc? August 25, 2007, 12:46 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap