>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by DoN. Nichols on March 7, 2007, 10:22 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Gunner on March 8, 2007, 1:20 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by DoN. Nichols on March 8, 2007, 10:07 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Ned Simmons on March 8, 2007, 10:13 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore