>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Cydrome Leader on June 22, 2007, 12:58 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by DoN. Nichols on June 22, 2007, 6:09 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Cydrome Leader on June 22, 2007, 12:58 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Martin H. Eastburn on June 22, 2007, 10:46 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Re: Special Adapter... | December 12, 2007, 3:07 pm |
| Re: Special Adapter... | December 13, 2007, 10:10 pm |
| Special Coolant-Thru Adapter Question - ER Style | July 13, 2007, 9:00 am |
| shank adapter, extension rod, button bit, thread bit,taper bit, taper rod, drill rod, drill bit, corss bit, chisel bit, DTH hammer drilling ,rock drill, drill tube, casing shoe, drilling tool, core bit, core barrel, ODEX, TUBEX, quarrying,mining equipment | September 8, 2006, 2:22 am |
| wtb: special tap | January 14, 2008, 11:10 am |
| CO2 adapter? | July 12, 2006, 1:01 am |
| special machines | March 27, 2007, 3:36 pm |
| Help with special micromter | April 26, 2007, 12:48 am |
| Handyman special | December 28, 2007, 2:30 am |
| OT: NRA special offers? | November 6, 2008, 9:45 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore