Posted by Dave, I can't do that on November 5, 2006, 11:01 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Jimi on November 5, 2006, 11:07 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Dave, I can't do that on November 5, 2006, 12:45 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by JayCups on November 5, 2006, 7:32 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Steve Ackman on November 6, 2006, 6:15 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | 3D Design CAD, 3DESIGN Boutique, other Jewelry design Software, other | January 17, 2008, 1:18 am |
| Porsche Design Dashboard - Porsche Design Watches | September 8, 2008, 4:55 am |
| You Guys said I should use 1/2" | September 6, 2008, 9:42 pm |
| OT - Any Woodworking Guys Here? | January 23, 2007, 10:30 am |
| Re: For you O Scope guys | June 3, 2007, 6:43 pm |
| Foil Hat Guys were right all along | September 18, 2007, 7:42 am |
| CNC Guys Question... | November 14, 2007, 2:23 pm |
| Re: OT-- Any of you guys using a "man purse"? | March 12, 2006, 5:51 am |
| Re: OT-- Any of you guys using a "man purse"? | March 12, 2006, 8:07 am |
| Re: OT-- Any of you guys using a "man purse"? | March 12, 2006, 8:14 am |
|
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore