General Metalworking - All aspects of working with metal.
|
|
|
|
|
Posted by James Lerch on September 16, 2007, 1:31 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by kfvorwerk@gmail.com on September 16, 2007, 7:45 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Trevor Jones on September 16, 2007, 9:51 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Mark F on September 16, 2007, 12:40 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Jeff Wisnia on September 16, 2007, 4:58 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | metal working | April 8, 2006, 7:37 am |
| now HERE is some real metal working | March 23, 2008, 2:24 am |
| POLITICS in metal working group | September 22, 2008, 12:38 pm |
| Old belt drive metal working shop | November 17, 2006, 10:30 pm |
| actually metal working related - paint type and color | February 20, 2008, 2:42 am |
| Blacksmith Day Saturday | May 19, 2008, 7:10 am |
| Metal project (sawmill) | November 7, 2008, 3:05 pm |
| Metal Mill and Lathe Project. | December 5, 2006, 11:31 pm |
| pyro project w/metal content | September 30, 2008, 12:57 pm |
| THIS WEEKEND, The Guthrie, OK Swapmeet! Saturday | May 14, 2008, 8:11 am |
|
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore