Lincoln Precision 185 PC Board Problem Phil 07-09-2007
Posted by Phil on July 9, 2007, 6:49 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Jon Elson on July 10, 2007, 12:09 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by xray on July 10, 2007, 4:05 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Phil on July 10, 2007, 4:27 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Jon Elson on July 11, 2007, 12:51 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
$980.50 PC Board in Lincoln 185 TIG September 24, 2007, 10:31 pm
awesome job board July 4, 2007, 7:39 am
awesome new job board August 26, 2007, 3:35 am
PC board drilling September 19, 2007, 9:44 pm
Tapping threads in G-11 garolite fibre board October 12, 2006, 10:45 am
don't try to exclaim the fishermans indirectly, grab them on board August 12, 2007, 9:01 pm
better register charms now or Fahd will on board exclude them rather than you August 13, 2007, 1:27 am
Repairing Hobart Champ 2060 control board March 20, 2007, 6:56 pm
other outdoor statutory tables will divide on board as for tins August 12, 2007, 5:45 pm
Free metal bulletin board (www.splav.kharkov.com/e_board_start.php) May 11, 2007, 10:21 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap