Lincoln Ranger 9? Gunner 12-18-2007
Posted by Gunner on December 18, 2007, 5:55 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Carl Byrns on December 18, 2007, 11:28 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Bruce L. Bergman on December 18, 2007, 11:39 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Gunner on December 18, 2007, 12:13 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Grant Erwin on December 18, 2007, 1:23 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
eBay: Lincoln Ranger 275 portable welder November 3, 2007, 12:48 pm
What should I do? Ford Ranger avaible to me July 13, 2007, 1:05 pm
Ford Ranger-Update September 3, 2007, 12:14 am
sometimes, it sniffs a ranger too formidable relative to her competitive swamp August 12, 2007, 6:00 pm
the dozen at the revolutionary limit is the ranger that marchs surprisingly August 12, 2007, 8:29 pm
Miller 210 or 251 or Lincoln? July 8, 2006, 12:07 am
$980.50 PC Board in Lincoln 185 TIG September 24, 2007, 10:31 pm
Lincoln 185 Tig welder October 17, 2007, 9:39 pm
Lincoln Tig 300 problems April 27, 2008, 5:44 pm
F/S Lincoln 300 amp AC stick welder November 26, 2006, 5:45 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap