Posted by Carl Byrns on December 20, 2007, 9:10 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Grant Erwin on December 20, 2007, 9:36 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Carl Byrns on December 21, 2007, 7:24 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Wayne Cook on December 18, 2007, 4:25 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Gunner on December 20, 2007, 5:20 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
eBay: Lincoln Ranger 275 portable welder November 3, 2007, 12:48 pm
What should I do? Ford Ranger avaible to me July 13, 2007, 1:05 pm
Ford Ranger-Update September 3, 2007, 12:14 am
Re: Ranger 9 charging circuit issue....?. September 15, 2008, 12:37 pm
Re: Ranger 9 charging circuit issue....?. September 15, 2008, 2:53 pm
Re: Ranger 9 charging circuit issue....?. September 15, 2008, 3:16 pm
Re: Ranger 9 charging circuit issue....?. September 15, 2008, 3:54 pm
sometimes, it sniffs a ranger too formidable relative to her competitive swamp August 12, 2007, 6:00 pm
the dozen at the revolutionary limit is the ranger that marchs surprisingly August 12, 2007, 8:29 pm
Miller 210 or 251 or Lincoln? July 8, 2006, 12:07 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap