>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by on October 2, 2006, 11:18 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Brian Lawson on October 3, 2006, 1:36 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by CPUjohn on October 4, 2006, 9:42 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by =?ISO-8859-1?Q?Nick_M=FCller?= on October 4, 2006, 10:16 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore