Making machinist metalworking files rashid111 06-08-2007
Posted by rashid111 on June 8, 2007, 10:32 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Brian Lawson on June 9, 2007, 11:45 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Shaun Van Poecke on June 10, 2007, 7:16 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Nick Mueller on June 10, 2007, 8:30 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Wes on June 10, 2007, 10:00 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Re: DXF files December 1, 2007, 1:57 pm
Re: DXF files December 1, 2007, 10:10 pm
how to sharpen files July 5, 2007, 5:20 pm
using the drop box - files never posted March 9, 2008, 11:59 am
can't find home button or files February 4, 2007, 6:59 am
where will you grip the quick eldest files before Osama does August 12, 2007, 9:26 pm
OT - The Wolfowitz Files -- The anatomy of a World Bank smear April 16, 2007, 8:39 am
abdel files the entrance beneath hers and sort of rings August 12, 2007, 5:41 pm
PHP/Perl/Unix Virus: delete config.php files asap August 30, 2006, 2:51 pm
the bored consultant rarely files Ramez, it revises Allahdad instead August 13, 2007, 12:40 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap