Material Hardness Scales... Joe AutoDrill 01-17-2008
Posted by Joe AutoDrill on January 17, 2008, 7:42 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ned Simmons on January 17, 2008, 10:13 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Joe AutoDrill on January 17, 2008, 10:16 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ned Simmons on January 17, 2008, 10:37 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Martin H. Eastburn on January 17, 2008, 11:28 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Request for material recommendation for a Titanium grade or similar lightweight material with high yield strength May 28, 2008, 10:24 pm
Anyone got a hardness tester? April 16, 2007, 12:34 pm
Odd metal hardness October 2, 2008, 11:43 am
Digital scales (DRO like) December 29, 2006, 3:15 am
DRO Scales from Littlemachineshop July 27, 2008, 8:30 pm
Weld hardness question March 28, 2007, 9:19 am
Hardness tester wanted May 2, 2007, 2:42 pm
Ames #2 hardness checker September 19, 2007, 9:54 pm
Bolt Hardness Question February 28, 2008, 2:32 am
Frugal SPC equipped scales for DRO August 5, 2007, 11:06 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap