Morse tapers please help mun 01-26-2007
Posted by mun on January 26, 2007, 12:03 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Steve Lusardi on January 27, 2007, 3:03 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by David Billington on January 27, 2007, 7:35 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by on January 27, 2007, 8:53 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by DoN. Nichols on January 29, 2007, 11:50 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Morse Tapers... May 9, 2006, 11:00 am
What are these tapers used for? September 28, 2006, 2:00 pm
Cutting accurate tapers within OD August 10, 2007, 7:50 pm
Sine Bar for setting lathe tapers -Atten Nick Mueller August 28, 2007, 3:27 pm
Weird adapter -- Morse #2 to Jacobs #5 June 29, 2007, 10:44 pm
Morse taper cutting any advice??? February 5, 2008, 7:26 pm
why is there a morse taper in the back end of my lathe spindle November 10, 2006, 1:05 pm
What's the difference between Morse Taper roughing and finishing reamers? June 6, 2007, 9:02 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap