>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by on May 6, 2007, 11:20 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Steve Russell on May 8, 2007, 5:26 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Nick Mueller on May 7, 2007, 4:03 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Steve Russell on May 8, 2007, 5:33 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore