Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by gcc on November 16, 2006, 2:09 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Keith Marshall on November 16, 2006, 9:53 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Bob Engelhardt on November 16, 2006, 11:47 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Keith Marshall on November 16, 2006, 11:40 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Lathe deals in Charlotte, NC area | August 27, 2007, 1:35 am |
| Lathe deals in Charlotte, NC area, Update | August 29, 2007, 11:07 am |
| Source for supplies | September 22, 2006, 7:46 am |
| Tools & supplies | May 12, 2008, 11:23 pm |
| Great Place to get the home hardware, tools and supplies | November 21, 2007, 9:24 am |
| for sale in Alachua/Gainesville FL: huge volume of shop stuff, tools supplies hardwares, other "guy stuff", 1, some, or all - PICKUP preferred | January 30, 2007, 11:17 am |
| Need source for high density foam in DFW area... | June 8, 2007, 12:20 pm |
| Re: Good source of angle iron in SF Bay Area? | June 7, 2008, 1:01 am |
| Semi OT: Need source for high density foam in DFW area... | June 8, 2007, 9:44 am |
| Semi OT: Need source for high density foam in DFW area... | June 8, 2007, 10:28 am |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore