Nitro shells in damascus barrel shotgun? Bad advise on RCM Honest A Babin 07-15-2007
Posted by Honest A Babin on July 15, 2007, 9:05 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by spaco on July 15, 2007, 10:53 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Wes on July 15, 2007, 11:39 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by John Martin on July 15, 2007, 11:45 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Carl Byrns on July 15, 2007, 12:29 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
[AD] Damascus Knives April 28, 2006, 6:34 pm
Re: FS -- 22,000 artillery shells 155mm April 8, 2008, 11:45 am
[OT] The Road to Damascus -- The strange new respect for Syria's Bashar Assad July 29, 2006, 11:28 am
OT - Al Qaeda's Travel Agent -- Damascus International Airport is a hub for terrorists August 22, 2007, 9:14 pm
Re: Help me fix my barrel; Tig or Mig? October 28, 2006, 7:27 pm
Sleeving a barrel August 11, 2007, 9:22 am
Anybody soldered in a barrel liner? March 14, 2007, 8:56 pm
OT - Shotgun scopes... February 17, 2007, 3:41 pm
Way OT Shotgun question September 11, 2007, 12:10 am
Shotgun chamber D reamer? July 5, 2008, 11:45 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap