Non-Destructive weld testing HotRod 08-04-2006
Posted by HotRod on August 4, 2006, 11:02 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Wayne Lundberg on August 4, 2006, 12:17 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Pete C. on August 4, 2006, 12:30 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by on August 4, 2006, 12:46 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
JB Weld March 17, 2006, 1:31 pm
JB weld October 30, 2008, 9:24 am
Weld positioners August 26, 2006, 6:24 pm
Re: gap in weld joints August 26, 2006, 6:39 pm
Best way to un-weld pipe? August 8, 2008, 1:38 pm
Testing newsgroup.. May 9, 2006, 7:29 pm
Re: Testing -- please delete May 9, 2006, 8:44 am
Testing welds April 22, 2008, 9:11 am
Testing the Waters... August 7, 2008, 11:03 am
TIG Weld Aluminum Filler Rod November 16, 2006, 8:38 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap