Posted by Bill Schwab on December 1, 2007, 12:17 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by BillM on December 1, 2007, 12:46 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Dave Hinz on December 1, 2007, 12:59 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Bill Schwab on December 1, 2007, 1:11 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Richard J Kinch on December 1, 2007, 2:19 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Lapping nylon | May 6, 2006, 4:09 pm |
| Nylon sling question | March 3, 2007, 6:22 pm |
| Nylon sling outcome | March 4, 2007, 12:01 pm |
| Looking for 1/2 inch square nylon bar | April 24, 2007, 8:16 pm |
| How to determine if Delrin, Teflon, Nylon...or? | May 8, 2007, 11:20 pm |
| Removing broken nylon bolts | July 5, 2007, 10:55 am |
| Ping tom Gardner! OT how to cut nylon brush:-) | December 27, 2007, 9:51 pm |
| Machining plastics: UHMW, Nylon, etc | September 16, 2008, 7:37 pm |
| De-burring inside tubes with nylon brushes | April 11, 2008, 7:35 pm |
| A new cheap source fo Delrin, UHMW, Teflon and Nylon | July 20, 2007, 10:15 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore