OSHA adhesive rant Boris Beizer 08-18-2006
Posted by Boris Beizer on August 18, 2006, 3:35 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Dave Hinz on August 18, 2006, 3:44 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Michael A. Terrell on August 18, 2006, 9:18 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Dave Hinz on August 18, 2006, 10:40 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Larry Jaques on August 19, 2006, 9:41 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Emergency O ring adhesive May 13, 2007, 5:35 pm
Adhesive Recommendation; Metal to Mylar? October 18, 2006, 4:36 pm
Silicone caulking as a metal adhesive May 11, 2008, 9:46 pm
Advice needed about choice of adhesive May 13, 2008, 11:21 pm
Adhesive for CNC machining of thin brass parts December 27, 2006, 3:29 pm
Application of adhesive to lead sheet metal January 23, 2007, 7:04 am
Re: Adhesive for bonding aluminum to cast iron November 27, 2007, 5:29 pm
Re: Adhesive for bonding aluminum to cast iron November 28, 2007, 1:41 am
Adhesive for bonding aluminum to cast iron November 27, 2007, 7:56 am
Rant mode on July 18, 2007, 11:33 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap