General Metalworking - All aspects of working with metal.
|
|
|
|
|
Posted by Ivan Vegvary on March 20, 2007, 10:52 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Ivan Vegvary on March 20, 2007, 10:54 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Lloyd E. Sponenburgh on March 20, 2007, 11:02 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Lloyd E. Sponenburgh on March 20, 2007, 1:16 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by on March 20, 2007, 11:05 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | OT but has some metal content | April 1, 2007, 8:20 pm |
| Serious Metal Content... | November 7, 2007, 3:51 pm |
| OT but a little metal content | February 22, 2008, 7:28 pm |
| OT: but with metal content | August 26, 2008, 10:50 pm |
| OT: jet man. metal content turbines | December 24, 2006, 11:47 pm |
| Check this out (Metal Content) | January 12, 2007, 11:18 pm |
| Don't steal from her (metal content) | April 23, 2007, 2:13 pm |
| OT -- Rednecks among us -- "some" metal content | October 12, 2007, 3:13 am |
| Shipbreaking (metal content) | November 7, 2007, 1:18 pm |
| OT: metal content -- gold | November 8, 2007, 2:31 pm |
|
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore