General Metalworking - All aspects of working with metal.
|
|
|
|
|
Posted by Don Foreman on May 1, 2007, 12:56 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Lloyd E. Sponenburgh on May 1, 2007, 1:58 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Richard J Kinch on May 1, 2007, 2:42 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by on May 1, 2007, 3:20 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Carl Byrns on May 1, 2007, 5:08 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | OT- Varmint Removal - (Sorry Nick M) | February 3, 2007, 3:33 pm |
| Nick, how are you doing with your scraping project? | February 24, 2007, 4:49 pm |
| nick,adidas,bamp | October 22, 2007, 9:11 pm |
| Question to nick mueller-carbide or hss? | May 4, 2007, 3:50 pm |
| OT - Poetry for Gunner. (Nick - dont read...) | October 19, 2006, 9:04 pm |
| Re: Ping: Nick Mueller re. technical German | April 29, 2008, 4:53 am |
| Student made a half sized tank (hey Nick!) | April 7, 2008, 4:11 pm |
| Sine Bar for setting lathe tapers -Atten Nick Mueller | August 28, 2007, 3:27 pm |
| machine paint? | December 8, 2006, 11:13 pm |
| Painting over old paint | February 3, 2007, 4:54 pm |
|
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore