Posted by Ben on February 16, 2007, 7:14 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Professor on February 16, 2007, 8:07 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Leo Lichtman on February 16, 2007, 8:23 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Ben on February 16, 2007, 9:11 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Martin H. Eastburn on February 16, 2007, 11:39 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Re: Question: Temp reached by black anodized aluminum in direct sun January 20, 2008, 12:01 pm
Re: Question: Temp reached by black anodized aluminum in direct sun January 19, 2008, 12:41 pm
Re: Question: Temp reached by black anodized aluminum in direct sun January 19, 2008, 2:42 pm
Re: Question: Temp reached by black anodized aluminum in direct sun January 19, 2008, 9:27 pm
Re: Question: Temp reached by black anodized aluminum in direct sun January 21, 2008, 4:54 pm
Cast Iron making question March 15, 2007, 6:23 pm
Waaaay OT: Question about seasoning Cast Iron March 19, 2006, 4:38 pm
Re: Strength of materials question: square tube vs angle iron April 14, 2008, 11:25 am
Re: Strength of materials question: square tube vs angle iron April 14, 2008, 11:44 am
Re: Strength of materials question: square tube vs angle iron April 15, 2008, 12:55 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap