Posted by Ignoramus17640 on September 16, 2006, 1:23 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Tom Gardner on September 16, 2006, 1:28 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Gunner on September 16, 2006, 1:55 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Ignoramus17640 on September 16, 2006, 2:00 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Larry Jaques on September 16, 2006, 10:02 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Bad Drill Bits!!! If you don't have a Darex Drill Doctor, read at your own risk of failing to understand. | December 12, 2007, 4:16 pm |
| MT2 drill bits vs. MT2 drill press | August 30, 2006, 2:33 am |
| More on drill bits over 5/8" | September 17, 2006, 7:36 pm |
| drill bits | September 9, 2007, 9:50 pm |
| drill bits | September 9, 2007, 9:51 pm |
| Re: jetting drill bits? | September 5, 2006, 7:56 pm |
| Grizzly drill bits | February 23, 2007, 10:09 am |
| Enco drill bits | December 11, 2007, 3:37 pm |
| Naming drill bits (HSS, HSS-E, HSS G, ...) | March 14, 2006, 4:42 pm |
| 1/8" or smaller drill bits | May 4, 2008, 11:09 am |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore