Re: Drills... Why? Paul K. Dickman 10-09-2007
Posted by Paul K. Dickman on October 9, 2007, 12:32 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Joe AutoDrill on October 9, 2007, 12:56 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Don Young on October 9, 2007, 9:51 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Paul K. Dickman on October 11, 2007, 1:30 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by David Harmon on October 11, 2007, 3:36 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Re: Drills... Why? October 9, 2007, 11:38 am
Re: Drills... Why? October 10, 2007, 3:58 pm
Re: Drills... Why? October 10, 2007, 10:53 pm
Drills... Why? October 9, 2007, 9:46 am
PCB drills update July 5, 2006, 6:23 pm
HF Step drills? Aye or Nay January 13, 2007, 10:57 pm
Cobalt Drills - right! February 23, 2007, 6:41 pm
Re: Cobalt Drills - right! February 24, 2007, 1:27 am
Heads UP Drills July 9, 2007, 10:16 pm
USA Drills deal July 10, 2007, 4:25 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap