Since welding group is still clogged up... Stuart Wheaton 09-01-2007
Posted by Stuart Wheaton on September 1, 2007, 3:34 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by F. George McDuffee on September 1, 2007, 3:57 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by cavelamb himself on September 1, 2007, 4:21 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Stuart Wheaton on September 1, 2007, 4:37 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by cavelamb himself on September 1, 2007, 5:09 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
grinding wheel clogged with aluminum January 16, 2007, 11:55 am
HVLP spray nozzles getting clogged up March 28, 2008, 2:33 am
New to group June 10, 2007, 3:37 pm
Need Help from the Group July 3, 2007, 1:09 pm
New to group September 15, 2007, 11:21 pm
joing my group March 9, 2007, 5:44 am
join me in this group June 1, 2007, 9:53 am
A question for the group August 23, 2007, 8:03 am
is it me? (group size?) March 4, 2008, 6:41 pm
Group question September 14, 2008, 1:18 am

Contact Us | Privacy Policy

XML SitemapXML Sitemap