Posted by azotic on May 20, 2007, 10:35 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Leon Fisk on May 23, 2007, 1:47 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by john on May 23, 2007, 6:02 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by DoN. Nichols on May 25, 2007, 1:33 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Leon Fisk on May 25, 2007, 1:49 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | McMaster-Carr Catalog #100 available | May 2, 2008, 3:15 pm |
| Re: MCMASTER-CARR Catalog number 1 | March 28, 2008, 7:49 pm |
| Re: MCMASTER-CARR Catalog number 1 | April 5, 2008, 10:58 pm |
| gonna move my MSC catalog to the basement today | May 28, 2007, 11:04 am |
| Interesting item I found in trailer parts catalog | April 24, 2008, 8:27 am |
| HandyMan DataBase Over 1,000,000 Specs | May 2, 2007, 12:18 am |
| HandyMan DataBase Over 1,000,000 Specs | June 21, 2007, 12:05 pm |
| HandyMan DataBase Over 1,000,000 Specs | July 10, 2007, 2:46 pm |
| HandyMan DataBase Over 1,000,000 Specs | October 29, 2007, 5:30 pm |
| HandyMan DataBase Over 1,000,000 Specs | December 4, 2007, 3:33 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore