>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Jordan on November 13, 2007, 4:28 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Jim Wilkins on November 13, 2007, 6:18 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Dom on November 13, 2007, 6:38 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Brian Lawson on November 13, 2007, 12:14 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Making taper attachment for lathe - what range of taper? | August 28, 2006, 8:33 am |
| shank adapter, extension rod, button bit, thread bit,taper bit, taper rod, drill rod, drill bit, corss bit, chisel bit, DTH hammer drilling ,rock drill, drill tube, casing shoe, drilling tool, core bit, core barrel, ODEX, TUBEX, quarrying,mining equipment | September 8, 2006, 2:22 am |
| Lock Bumping | October 18, 2006, 9:46 pm |
| Broken Lock Key Extraction | January 22, 2007, 10:28 pm |
| Hardened lock shackles? | April 29, 2007, 12:04 am |
| set screws lock against threads ?? | December 1, 2007, 7:36 pm |
| Dremel EZ Lock 1-1/2 Cut-off Wheels? | March 1, 2008, 11:46 am |
| Carriage Lock on Clausing 6903 | October 19, 2006, 2:00 am |
| Adding spindle lock to Sieg X3? | August 2, 2007, 1:00 pm |
| Logan Spindle Cam Lock adapter | January 18, 2008, 5:41 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore