>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Cydrome Leader on October 1, 2006, 11:55 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by on October 2, 2006, 2:37 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Jim Stewart on October 2, 2006, 2:52 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
Posted by Wild Bill on September 30, 2006, 11:58 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some >pipe flux with zinc chloride but it is only 8%. > > -- > Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore