Tapping hole in brass question RoyJ 12-01-2007
Posted by RoyJ on December 1, 2007, 7:26 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Snag on December 1, 2007, 7:42 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Jeff R. on December 1, 2007, 8:02 pm
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by RoyJ on December 2, 2007, 10:16 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Posted by Lew Hartswick on December 2, 2007, 10:28 am
Please log in for more thread options

>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore


Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.

Cheers
--
Jeff R.




Similar ThreadsPosted
Torque when tapping 1/4" NPT in brass July 12, 2006, 9:44 pm
thinish brass: hole saw okay? September 6, 2007, 5:31 pm
Tapping Question - Not Directly Related to Metal. October 4, 2007, 12:01 pm
Boring a hole question... February 28, 2008, 12:50 am
Re: Tapping aluminum (or tapping on wood?) December 15, 2007, 9:13 pm
Re: Tapping aluminum (or tapping on wood?) December 15, 2007, 10:35 pm
Re: Tapping aluminum (or tapping on wood?) December 17, 2007, 1:17 am
Feed Rate Question - Small Hole November 8, 2006, 3:01 pm
Need help with 2 1/4 - 8 thread. Minimun hole size question October 31, 2008, 12:51 pm
Plastic Drilling Question - Small Hole Process.... August 19, 2008, 3:51 pm

Contact Us | Privacy Policy

XML SitemapXML Sitemap