>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Don Foreman on January 30, 2007, 1:39 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Ignoramus23017 on January 30, 2007, 1:49 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Don Foreman on January 30, 2007, 4:07 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Bruce L. Bergman on January 30, 2007, 11:44 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Crankshaft Heat Treatment | November 23, 2006, 12:10 pm |
| Jenolite rust treatment. | June 16, 2007, 10:48 am |
| heat treatment tools | December 27, 2007, 3:39 pm |
| pre and post heat treatment for TIG welding | November 30, 2007, 8:58 pm |
| 1095 steel heat treatment | May 4, 2008, 10:39 pm |
| Need for steel that is reasonably easy to work with and that has a yield strength of 75,000 to 85,000 PSI prior to heat treatment | August 4, 2006, 4:36 pm |
| [Trailer project] Welded adjustable towing eye holder to trailer tongue | January 21, 2007, 6:13 pm |
| new patent pending laser beam treatment/shooting for military or industry, product anit counterfying, hologram, company logo, etc. | February 11, 2007, 8:31 pm |
| trailer 101? | October 21, 2006, 9:56 pm |
| Got a new trailer | July 4, 2007, 7:16 pm |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore