>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Richard Ferguson on December 30, 2006, 1:48 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Mickey Feldman on December 30, 2006, 2:41 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Pete T on December 30, 2006, 2:20 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Mickey Feldman on December 30, 2006, 2:37 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | Vacuum pump advice please, for casting, investing, etc. | April 16, 2006, 7:30 pm |
| FA: hydraulic pump, right angle gear drive, very heavy caster, Oil pump from large milling machine | April 26, 2006, 1:29 am |
| ISLAMIC TRASH ATTACK ORIGIN | August 13, 2007, 1:59 am |
| 10" Atlas lathe purchase trash/treasure? | June 3, 2007, 9:20 pm |
| Re: HAMMERHEAD '07: Worthless White Trash Pride World Wide | September 10, 2007, 12:18 pm |
| When to run oiler pump during CNC cycle? Bed lift due to oiler pump. | October 27, 2006, 3:34 pm |
| Anyone tried this pump for coolant? | January 2, 2007, 5:59 am |
| Help me ID a mystery pump | August 13, 2007, 11:50 pm |
| FA: Gast pump, anyone? | April 24, 2006, 1:05 am |
| Re: anyone have a clue what this pump was used with? | March 23, 2006, 12:44 am |
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore