Posted by Martin Riggins on October 17, 2006, 12:54 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Gunner Asch on October 17, 2006, 3:17 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by Joseph Gwinn on October 17, 2006, 10:54 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by on October 18, 2006, 3:58 pm
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
|
Posted by =?ISO-8859-1?Q?Nick_M=FCller?= on October 17, 2006, 4:15 am
Please log in for more thread options
>I will give that a try if I can't find the ammonium version. I have some
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore
Don't forget, you can make your own (much stronger) by killing some
hydrochloric acid with a handful of zinc. (I presume you have zinc lying
around if you're galvanising stuff.) Otherwise use scrap galvanised steel.
Cheers
--
Jeff R.
|
| Similar Threads | Posted | | What is the difference in the construction of a 1/3 vs a 1/2 HP AC motor that makes for the difference in power output. | November 21, 2006, 10:58 pm |
| fs: anyone need a couple of 440V VFDs (1 HP) | April 13, 2008, 1:35 pm |
| VFDs, belt drive, and a lathe | July 26, 2007, 8:15 pm |
| Digital scales and VFDs (and YADRO) | May 12, 2006, 1:27 pm |
| 1045, 4140, What Is The Difference? | February 27, 2007, 10:47 pm |
| Telling the difference between C2 & C5 carbide? | May 4, 2007, 5:16 pm |
| The difference... is the price of their toys... | April 3, 2006, 9:30 am |
| cross slide vise - what is the difference | May 12, 2006, 3:04 am |
| What's the difference between Morse Taper roughing and finishing reamers? | June 6, 2007, 9:02 am |
| If you will reduce Abdul's cluster by way of distributions, it will greedily recover the difference. | August 14, 2007, 1:31 am |
|
|
|
Yahoo! 
Google 
Windows Live 
del.icio.us 
digg 
Netscape 
XML Sitemap
>pipe flux with zinc chloride but it is only 8%.
>
> --
> Glenn Ashmore